GDC thin-film deposited at 500°C (GDC-H) was compared to a film prepared at room temperature (GDC-R). Figure 1 a,b respectively shows the XPS spectra of Ce 3d and Gd 4d core levels of …

Download scientific diagram | XPS spectra of (a) Ce 3d, (b) Gd 4d, and (c) O 1s core levels for the as-deposited GDC films on 8YSZ substrates. from publication: A facile method for the...

2024年8月16日 · The XPS spectra of Gd splits into two spin orbit states: Gd 4d 3/2 and Gd 4d 5/2 for which the characteristic peaks are located at 146.16 eV and 141.01 eV respectively.

Collect principal Gd (4d) peak as well as Gd (3d). Long time exposures (high dose) to X-rays can degrade various polymers, catalysts, high oxidation state compounds

This suggests that our Gd-based nanoparticles exhibit a relatively higher relaxivity, indicating their potential for enhanced contrast and improved efficiency in magnetic resonance imaging ...

2016年5月20日 · The XPS spectrum for Gd 4d (Fig. 4 (d)) reveals that the characteristic Gd 4d peaks centered at 141.5 and 147.7 eV could be attributed to Gd 4d 5/2 and Gd 4d 3/2, …

2019年5月1日 · X-ray photoemission spectrum of Gd 4d core level shows a wide spread structure over 30 eV [19]. This shape is caused by the strong 4d - 4f Coulomb, exchange and spin-orbit …

X 射线光电子能谱 (XPS) 勘测光谱揭示了铜、钆和氧等基本元素。 Gd4d 的峰值拟合在 143.6 和 155.8 eV 结合能处显示出两个主要峰值，分别对应于 4d 5/2和 4d 3/2之间 12.2 eV 的自旋轨道 …

2011年2月15日 · In this paper, we report a facile method for synthesis of ultra small (1–3 nm) gadolinium oxide (Gd 2 O 3) nanoparticles using citric acid (CA) as a capping agent. The …

X-ray photoelectron spectra (XPS) predict the electronic states, bond energies, suitable stoichiometry, and oxidation states of the compositions. The XPS spectra of Ce 3d, O 1s, and …